植物源木材防腐剂微囊制备及缓释动力学研究

It has always been a hot spot of plant source wood preservatives in wood protection field, but existing researches were mostly about performance evaluation of antifungi component, research about how to improve control-released of active ingredient and it's dynamic mechanism were little. On the basis of previous research on plenty plant resource preservations, this project takes the microencapsulation of plant resource preservations as a starting point, with a resin wall, controls the microencapsulation process, size distribution，cladding.rate and wall layer structure by microencapsulation condition, to find the relativity between diameter of microcapsule and flow and deposition of it in timber, microcapsule system which has a better release properties. The analytical framework of drug delivery was based. The active of preservative could released for it protract live-span and improve the corrosion periods. It will also offer a reference to develop a new type of plant source wood preservatives.

植物源木材防腐剂开发是木材保护学领域的研究热点之一，但已有研究多停留在植物活性成分抑菌性能的评价上，对如何提高活性成分的缓释性能，揭示其动力学机制仍鲜见报道。在前期研究基础上，本课题拟采用印楝提取物作为植物源木材防腐剂微囊的囊芯，制备植物源防腐剂微囊缓释制剂，通过控制微囊的包覆结构，揭示微囊粒径尺寸与其在木材中流动性、沉积性的关系，从微观角度出发总结微囊缓释过程的受控规律，并建立系统的药物释放动力学分析体系，使活性成分得到缓慢释放，达到延长防腐时效，提高环境稳定性的效果。项目的研究为环保型木材防腐剂开发领域提供一个新思路。

木材的多细胞生物质特性在具有优异应用性能的同时，也容易被腐朽菌降解而导致大量资源浪费。因此，通过防腐处理提高木材利用率是至关重要的。但是，在环境问题日益尖锐的情况下，具有环境友好、易降解、原料丰富等优点的植物源防腐剂成为研究热点。但是植物活性成分对环境敏感的缺点限制了这项研究的应用。本项目开展“植物源木材防腐剂微囊制备及缓释动力学研究”对于发展环境友好的植物源木材防腐剂是提供了思路。通过本项目的研究制备了一种以印楝种子提取物作为囊芯、以三聚氰胺脲醛树脂作为壁材的植物源木材防腐剂微囊，通过对微囊的性能研究确定了最佳的制备工艺。微囊粒径分布整体呈正态分布，平均粒径为1.97μm，微囊平均壁厚159.5nm。用该植物源防腐剂微囊处理的试材达到了强耐腐等级。具有良好的环境稳定性，抗喷淋能力最强，抗紫外和抗凝露能力次之，但是高于印楝种子提取物的环境稳定性，达到缓释的目的。项目的研究为木材防腐剂在木材中的缓释性能评价提供科学参考。