Many inorganic ultraviolet blocking agent due to the larger particle size or the shielding properties of the transparency of the material of the strong influence; organic ultraviolet blocking agent and there is the disadvantage of poor light and heat stability and therefore more excellent performance study cosmetic UV barrier material is verynecessary. Talcs inorganic water-based materials such as composition, structure, microstructure adjustable features, by the intercalation method of assembling the organic UV absorbers and their recombination, so that the preparation of the novel nanometer ultraviolet barrier material becomes possible.Compatibility study of the present application focuses on research work carried out from the following three aspects: (1) Laminates elements and proportions of the optical functional layer between the regulation (2) of the object through the modification of grain surface, the hydrotalcite-like material as a sunscreen.; (3) finished sunscreen, sunscreen performance studies, efficacy, usability evaluation. Controllable Preparation of performance-oriented, strengthening the cosmetics hydrotalcite class UV barrier material controllable preparation, in-depth study of the interdependent relationship between the microstructure and UV barrier properties, to solve this kind of material-oriented, UV barrier properties in key scientific , who promote the efficient and safe cosmetics with UV absorbers research has important potential applications.

目前许多无机紫外线阻隔剂由于粒径较大或遮蔽性过强影响材料的透明性；有机紫外阻隔剂又存在光热稳定性较差的缺点，因此研究性能更加优良的化妆品用紫外阻隔材料是十分必要的。基于无机水滑石类材料组成、结构等微观结构可调的特点，通过插层组装方法将有机紫外吸收剂与其复合，从而使制备新型纳米级紫外阻隔材料成为可能。本申请着重从以下三个方面开展研究工作：（1）层板元素及比例、层间光功能客体的调控（2）通过晶粒表面改性，对水滑石类材料作为防晒剂的配伍性研究；（3）实现防晒霜成品，防晒剂性能研究，功效性、实用性评价。以性能为导向，强化化妆品用水滑石类紫外阻隔材料的可控制备，深入研究微观结构与紫外阻隔性能之间的依存关系，解决该类材料为导向的可控制备、紫外阻隔性能中的关键科学问题，对于推动高效安全的化妆品用紫外吸收剂的研究具有重要意义和潜在应用前景。

随着地球环境不断恶化，臭氧层的破坏日趋严重，地面接受的紫外线辐射量不断增加，给人类带来的影响已被世界范围所认识，如何防范紫外线辐射已引起人们的广泛关注。目前许多无机紫外线阻隔剂由于粒径较大或遮蔽性过强影响材料的透明性；有机紫外阻隔剂又存在光热稳定性较差的缺点，因此研究性能更加优良的化妆品用紫外阻隔材料是十分必要的。本项目以紫外阻隔性能为导向，系统研究了水滑石类材料组成、结构、微观形貌与性能之间的依存关系。研究发现当水滑石主体层板引入钛元素后，由于降低了带隙宽度，使得此类材料的紫外阻隔性能显著提高（较镁铝或锌铝水滑石可提高10倍）。相比传统的无机阻隔剂二氧化钛和氧化锌，ESR表明该材料具有更低的光催化活性，即安全性更高。曾经广泛使用的对氨基苯甲酸由于存在潜在的致敏性，现已被法国禁止添加在防晒霜中。本研究中将其与锌钛水滑石复合，uv-vis数据表明不但紫外吸收性能提高，而且提高了有机物自身的光热稳定性，并且避免其与皮肤直接接触，提高产品的安全性。将亲油性的紫外吸收剂肉桂酸与锌钛水滑石复合，并添加到防晒霜中，较空白产品的紫外吸收能力显著提高，TG-DTA、ESR等数据表明该新型防晒剂较肉桂酸自身的稳定性、安全性也显著提高。综上所述，本研究通过插层组装构筑的无机-有机超分子材料较好的解决了目前单一无机、有机防晒剂各自的弊端，发展一类稳定的、安全的、配伍性好的LDH基复合防晒材料。对于推动高效安全的化妆品用紫外吸收剂的研究具有重要意义和潜在应用前景。