带有抗菌基团的丙烯酸酯单体的合成及其在树脂基口腔材料抗菌改性上的应用

The resin-based dental materials commonly used in restorations result in more plaque accumulation than other materials. In this study, new monomers with antibacterial activity were synthesized by combining an antibacterial agent (bis-quaternary ammonium salts or quaternary phosphonium salts) and methacryloyl group. The monomer was incorporated into resin-based dental materials to develop non-releasing antibacterial materials. The relationship between antibacterial activity and chemical structure of antibacterial monomer was investigated, and the influence of incorporation of antibacterial monomer on the chemical properties, mechanical properties and biocompatibility of dental materials was also studied. The results of this study was attempted to not only improved the antibacterial activity of resin-based dental materials, but also be applied to other resin-based medical materials as well as industrial materials.

树脂基口腔材料以其优异的性能在口腔医学中得到了越来越广泛的应用，但该类材料抗菌性能差，易被病菌感染而导致口腔疾病发生已是一个常见且不容忽视的问题。本项目拟通过分子设计的方法，设计合成具有抗菌基团（双季铵盐基团或季膦盐基团）和可聚合基团（甲基丙烯酸酯基团）的抗菌单体。该单体化学结构中的可聚合基团保证了抗菌单体可以通过共聚合牢固结合到树脂基口腔材料中，避免了抗菌性能的"突释效应"，且基本不会影响树脂基口腔材料的固化过程和固化后的性能。通过研究抗菌单体的定量结构- - 活性关系以及对树脂基口腔材料的抗菌性能、化学性能、物理机械性能和生物相容性等各方面的影响，期望不仅可以解决树脂基口腔材料在临床应用中的细菌感染问题，而且还可以推广应用于其它树脂基生物材料乃至工业材料的抗菌改性。

树脂基口腔材料以其优异的性能在口腔医学中得到了越来越广泛的应用，但该类材料抗菌性差，易被病菌感染而导致口腔疾病发生已是一个常见且不容忽视的问题。.本研究通过分子设计的方法，设计并合成具有抗菌官能团（双季铵盐基团或季磷盐基团）和双可聚合官能团（甲基丙烯酸酯基团）的抗菌单体。抗菌官能团（双季铵盐基团或季磷盐基团）中的阳离子氮和阳离子磷赋予了口腔材料良好的抗菌性能。可聚合官能团（甲基丙烯酸酯基团）可以确保以化学键结合到口腔材料中，避免突释效应。采用双可聚合官能团提高了抗菌单体由于没有完全化学结合而溶出的问题。本研究中合成的抗菌单体赋予树脂基口腔材料长久的抗菌性，提高了抗菌效率和单体转化率，减少了抗菌剂的毒副作用以及对材料的物理机械性能的负面影响。.研究结果表明，几种单体的合成路线可行，可以得到高纯度的产物。定量结构——活性关系表明，双季铵盐的抗菌活性与单季铵盐相差不大，但是季膦盐的抗菌活性要高于季铵盐。一定比例抗菌材料的加入对基托树脂的化学性能和物理机械性能没有显著性影响。.本研究证明了可以通过分子设计的方法制备一些新型的具有良好抗菌性能的树脂基材料。本研究不仅可以解决树脂基口腔材料在临床应用中的细菌感染问题，而且还可以推广应用于其它生物材料乃至工业材料的抗菌改性。