水氯镁石和芒硝多元低温熔盐复合相变储能材料的制备和机制研究

The related theory and mechanism of multi-phase low-temperature molten salt phase change composite will be investigated with bischofite and mirabilite as a main component; the contents include: establishment of data base of research; to find ways to eliminate or suppress the phenomenon of supercooling and phase separation in the transformation process; to prepare phase change composites with good phase transition stability, reversibility and phase transition enthalpy at 15℃~35℃ based on bischofite and mirabilite; To study and explore new energy saving composites with good compatibility, structure stability, heat preservation and so on during the forming process of phase change energy storage material and base material.

研究以水氯镁石和芒硝为主成分的多元低温熔盐复合相变储能材料的相关理论和机理；建立相关研究的数据信息库；研究在相变过程中产生过冷和相分离现象的原因，找到消除或抑制这些现象的方法。制备在15℃~35℃范围内具有良好相变稳定性、可逆性和相变焓的以水氯镁石为主成分的复合相变储能材料，研究开发以水氯镁石和芒硝为主成分的相变储能材料与基体材料在共混成形过程中保持材料具有良好相容性、结构稳定性、保温节能性等基本性能的新型节能材料。

本项目完成了对水氯镁石、芒硝等无机水合盐体系采用TG-DSC方法进行单组分、多组分混合物的相变温度、相变焓的测定，并依据实验数据绘制了温度变化对试样质量、能量变化的响应曲线，制作了描述相关变化规律的相图。.（1）用TG-DSC法研究水氯镁石、芒硝的脱水反应规律；.（2）用TG-DSC法研究二元贮冷、储能水合盐的相变规律；.（3）进行了多元低温熔盐储能材料储能密度及热导率分析；.（4）进行了超声辅助溶胶-凝胶法制备定形多元低温熔盐相变储能材料；.（5）用曲面响应法研究多元低温熔盐的成分组成、成分比例与相变温度、相变焓的相关性；.（6）采用XRD、SEM等表征方法对水氯镁石和芒硝等无机水合盐体系进行相变中间产物的晶体形貌分析。